Properties |
Unit |
ASTM Test Method |
Sheet Extrusion Grades |
Antistatic
|
|
|
|
|
|
|
SE-22M |
SE-22 |
SE-20P |
SE-45 |
SE-32 |
SE-32M |
PT-45 M |
| Physical |
| Sp.Gravity |
|
D-792 |
1.04 |
1.045 |
1.045 |
1.04 |
1.045 |
1.045 |
1.045 |
| Mould Shrinkage |
% |
D-955 |
0.4-0.5 |
0.4-0.5 |
0.40-0.5 |
0.4-0.5 |
0.4-0.6 |
0.4-0.60 |
0.4-0.60 |
| |
|
|
|
|
|
|
|
|
|
| Mechanical Properties |
| Tensile strength,@yield |
Kg/sq.cm. |
D-638 |
410 |
450 |
450 |
390 |
400 |
440 |
390 |
| Type-I 3.2mm, 5mm Speed |
|
|
|
|
|
|
|
|
|
| Flexural Strength@yield |
Kg/sq.cm. |
D-790 |
560 |
640 |
660 |
560 |
570 |
645 |
490 |
| 6.4mm |
|
|
|
|
|
|
|
|
|
| Flexural Modulus |
Kg/sq.cm. |
D-790 |
19,500 |
21000 |
22,500 |
19,000 |
19,500 |
20,500 |
18,000 |
| 6.4mm |
|
|
|
|
|
|
|
|
|
| ROCKWELL Hardness |
R Scale |
D-785 |
107 |
110 |
113 |
105 |
106 |
108 |
102 |
| Izod Impact, Notched |
Kgfcm/cm. |
D-256 |
46 |
36 |
37 |
58 |
46 |
45 |
52 |
| 3.2mm |
|
|
|
|
|
|
|
|
|
| Izod Impact, Notched |
Kgfcm/cm. |
D-256 |
36 |
30 |
30 |
45 |
36 |
35 |
38 |
| 6.4mm |
|
|
|
|
|
|
|
|
|
| Thermal Properties |
| HDT (Method A) |
Deg C |
D-648 |
94 |
94 |
94 |
92 |
92 |
94 |
88 |
| @ 18.56 Kgf/sq.cm. |
|
|
|
|
|
|
|
|
|
| Annealed |
|
|
|
|
|
|
|
|
|
| VST (Method B) |
Deg C |
D1525 |
107 |
106 |
106 |
103 |
104 |
106 |
99 |
| |
|
|
|
|
|
|
|
|
|
| Melt Flow Index |
| Melt Flow Index |
Gm/10 Min |
D-1238 |
8 |
10 |
6 |
5 |
7 |
7 |
8 |
| 220 Deg c/10 kg |
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
| Flame Class Rating
|
| Flammability @ 3.2 mm |
|
UL-94 |
HB |
HB |
HB |
HB |
HB |
HB |
HB |
| |
|
|
|
|
|
|
|
|
|
| Characteristic Features |
|
|
Sheet Extrusion grade for profile & Doors |
ABS Pipe Grade |
Super high and Very High Impact Sheeting grades for Automobile & Luggage Applications |
Antistatic Cop Sleeves Application |
|
|
|
|
|
|
|
|
|
|
All the values sited above are indicattive values recorede on ASTM injection molded specimen and not be construed as product specifications |
|