Abstron Specility Grades,Alloys and Reinforced |
| |
Properties |
Unit |
ASTM Test
Method |
Glass Reinforced Grades |
ABS-PC Alloys |
Flame Retardent ABS Grades |
IMG-1115 |
IMG1120 |
IMG1130 |
IMGS20 |
IMC-45 |
IMC-45M |
IMC-45 V |
IMC-45 FR V2 |
AN-450 EVM |
AN-450M |
AN-312 |
AN480V2 |
SE-22 FR |
| Other Properties |
| Sp.Gravity |
|
D-792 |
1.22 |
1.22 |
1.25 |
1.24 |
1.12 |
1.13 |
1.14 |
1.16 |
1.17 |
1.17 |
1.17 |
1.16 |
1.2 |
| Mould Shrinkage |
% |
D-955 |
0.2-0.4 |
0.2-0.40 |
0.2-0.4 |
0.2-0.4 |
0.5-0.70 |
0.5-0.70 |
0.5-0.70 |
0.4-0.60 |
0.4-0.6 |
0.4-0.6 |
0.4-0.6 |
0.4-0.6 |
0.4-0.6 |
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Mechanical Properties |
| Tensile strength,@yield |
Kg/sq.cm. |
D-638 |
580 |
630 |
670 |
750 |
530 |
550 |
600 |
500 |
420 |
420 |
400 |
500 |
380 |
| Type-I 3.2mm; 5mm/min |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Flexural Strength@yield |
Kg/sq.cm. |
D-790 |
820 |
900 |
970 |
1000 |
800 |
850 |
900 |
700 |
580 |
580 |
550 |
710 |
590 |
| 6.4mm |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Flexural Modulus |
Kg/sq.cm. |
D-790 |
40,000 |
42,000 |
46000 |
46,000 |
22,500 |
23,500 |
24,500 |
24,000 |
21,000 |
21000 |
18,000 |
21,500 |
22,000 |
| 6.4mm |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| ROCKWELL Hardness |
R Scale |
D-785 |
115 |
115 |
115 |
118 |
112 |
113 |
115 |
114 |
106 |
106 |
105 |
111 |
106 |
| Izod Impact, Notched |
Kgfcm/cm. |
D-256 |
7 |
7 |
6 |
6 |
56 |
60 |
65 |
45 |
18 |
18 |
20 |
15 |
23 |
| 3.2mm |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Izod Impact, Notched |
Kgfcm/cm. |
D-256 |
6 |
6 |
5 |
4 |
40 |
45 |
50 |
N/A |
14 |
14 |
18 |
13 |
20 |
| 6.4mm |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Glass Contents |
|
|
15% |
20% |
30% |
20% |
|
|
|
|
|
|
|
|
|
| Thermal Properties |
| HDT (method A) |
Deg C |
D-648 |
105 |
105 |
108 |
109 |
105 |
110 |
120 |
96 |
88 |
88 |
88 |
90 |
82 |
| @ 18.56 Kgf/sq.cm. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Annealed. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| VST (method B) |
Deg C |
D1525 |
115 |
115 |
120 |
120 |
115 |
120 |
130 |
105 |
99 |
99 |
98 |
99 |
95 |
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Rheological Properties |
| Melt Flow Index |
Gm/10 Min |
D-1238 |
15 |
12 |
10 |
16 |
13 |
10 |
9 |
30 |
63 |
63 |
50 |
38 |
26 |
| 220 Deg c/10 kg |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Flame Class Rating |
| Flammability @ 3.2 mm |
|
UL-94 |
HB |
HB |
HB |
HB |
HB |
HB |
HB |
V-2 |
V0 |
|
V0 |
V2 UL certified at 2.2 mm |
V0 UL certified at 1.6 mm |
| |
|
|
|
|
|
|
|
|
|
at 3.2mm |
at 3.2 mm |
at 3.2 mm |
Products compliant |
|
|
|
|
|
|
|
|
|
|
|
RoHS |
|
|
|
| Characteristic Features |
|
|
Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temeperature |
ABS-polycarbonate alloys for High service temperature appplications |
ABS-Polycarbonate alloy with Flame Retardancy, general purpose FR-ABS and Sheet Extrusion Grade with FR feature.Cleck heare 94 V0 and V2 specifications. Some of the grades are UL certified |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
All the values sited above are indicattive values recorede on ASTM injection molded specimen and not be construed as product specifications |
|